Mechanisms of stacking fault tetrahedra destruction by gliding dislocations in quenched gold

, , &
Pages 581-597 | Received 15 Sep 2007, Accepted 04 Jan 2008, Published online: 18 Mar 2008
 

Abstract

The destruction processes of stacking fault tetrahedra (SFTs) induced by gliding dislocations were examined by transmission electron microscopy (TEM) in situ straining experiments for SFTs with edge lengths ranging from 10 to 50 nm. At least four distinct SFT destruction processes were identified: (1) consistent with a Kimura–Maddin model for both screw and 60° dislocations, (2) stress-induced SFT collapse into a triangular Frank loop, (3) partial annihilation leaving an apex portion and (4) complete annihilation. Process (4) was observed at room temperature only for small SFTs (∼10 nm); however, this process was also frequently observed for larger SFTs (∼30 nm) at higher temperature (∼853 K). When this process was induced, the dislocation always cross-slipped, indicating only screw dislocations can induce this process.

Acknowledgements

This research was sponsored by the Office of Fusion Energy Sciences, US Department of Energy, under contract DE-ACO5-00OR22725 with UT-Battelle, LLC. We thank Dr Thak Sang Byun for valuable comments.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.