Threshold stress for superplasticity in solid solution magnesium alloys

Abstract

The effect of alloying elements on the threshold stress for superplasticity was investigated using two binary solid solutions, namely, Mg–Al and Mg–Y alloys. Both alloys exhibited superplasticity, and in spite of the absence of fine particles showed threshold-stress-like behavior. Different origins were suggested for the threshold-stress-like behavior after considering grain growth during deformation. The threshold-stress-like behavior in Mg–Al alloys originates from the effects of microstructural instability (grain-growth hardening). On the other hand, analysis of grain-boundary segregation suggested that the threshold-stress-like behavior in Mg–Y alloy originates from the segregation of yttrium in grain boundaries and its interaction with grain-boundary dislocations.

Keywords:

• superplasticity
• magnesium alloy
• grain boundary interface
• first-principles calculation
• threshold stress

Acknowledgements

This work was supported by KAKENHI (20760483 and 20560688).