Abstract
Small imperfections in a crystal cause diverse patterns of contrast on an electron micrograph. The shape of these patterns is calculated by a new method, the result being a simple algebraic function of x and y. Detailed results are given for the symmetrical centre of pressure, for double forces and for prismatic dislocation loops in aluminium, copper and beta brass.