Abrasion Resistance and Tensile Behavior of Woven Bi-voltine Silk Fabrics

ABSTRACT

Fabric-to-fabric abrasion was carried for soft silk fabrics at dry and wet state under 500 and 1000 cycles and abraded samples were evaluated for bursting strength. Abrasion resistance of soft silk was also evaluated with wool abradant to arrive at the standard abrasion cycle. Yarn samples were removed from the abraded areas of 25%, 50%, and 75% of standard abrasion cycles of soft silk fabrics and then tensile strength was evaluated at dry and wet condition to understand the extent of damage happened due to abrasion.

摘要

对柔软真丝织物进行了干湿状态下500次和1000次循环的织物对织物的磨损试验，并对磨损后的样品进行了爆裂强度评价. 并用羊毛的耐磨性达到了标准. 从25%、50%和75%的标准磨损周期的磨损区域去除纱线样品，然后评估干、湿条件下的拉伸强度，以了解磨损造成的损伤程度.

KEYWORDS:

• Soft silk
• bivoltine
• cocoon
• abrasion
• tensile strength
• bursting strength

关键词:

• 软丝
• 双壳
• 茧
• 磨损
• 抗拉强度
• 爆破强度