Abstract
New natural rubber (NR)/nitrile butadiene rubber (NBR)/hindered phenol (AO-80) composites with high-damping properties were prepared in this study. The morphological, structural, and mechanical properties were characterized by atomic force microscopy (AFM), polarized Fourier transform infrared spectrometer (FTIR), dynamic mechanical thermal analyzer (DMTA), and a tensile tester. Each composite consisted of two phases: the NR phase and the NBR/AO-80 phase. There was partial compatibility between the NR phase and the NBR/AO-80 phase, and the NR/NBR/AO-80 (50/50/20) composite exhibited a co-continuous morphology. Strain-induced crystallization occurred in the NR phase at strains higher than 200%, and strain-induced orientation appeared in the NBR/AO-80 phase with the increase of strain from 100% to 500%. The composites had a special stress–strain behavior and mechanical properties because of the simultaneous strain-induced orientation and strain-induced crystallization. In the working temperature range of a seismic isolation bearing, the composites (especially the NR/NBR/AO-80 (50/50/20) composite) presented a high loss factor, high area of loss peak (TA), and high hysteresis energy. Therefore, the NR/NBR/AO-80 rubber composites are expected to have important application as a high-performance damping material for rubber bearing.
Acknowledgments
We would like to thank Dr Tung W. Chan from the Department of Materials Science and Engineering at Virginia Polytechnic Institute and State University for improving the written English.
Disclosure statement
No potential conflict of interest was reported by the authors.