Enhancement of antibacterial properties of Ag nanorods by electric field

Abstract

The effect of an electric field on the antibacterial activity of columnar aligned silver nanorods was investigated. Silver nanorods with a polygonal cross section, a width of 20–60 nm and a length of 260–550 nm, were grown on a titanium interlayer by applying an electric field perpendicular to the surface of a Ag/Ti/Si(100) thin film during its heat treatment at 700 °C in an Ar+H₂ environment. The optical absorption spectrum of the silver nanorods exhibited two peaks at wavelengths of 350 and 395 nm corresponding to the main surface plasmon resonance bands of the one-dimensional silver nanostructures. It was found that the silver nanorods with an fcc structure were bounded mainly by {100} facets. The antibacterial activity of the silver nanorods against Escherichia coli bacteria was evaluated at various electric fields applied in the direction of the nanorods without any electrical connection between the nanorods and the capacitor plates producing the electric field. Increasing the electric field from 0 to 50 V cm⁻¹ resulted in an exponential increase in the relative rate of reduction of the bacteria from 3.9×10⁻² to 10.5×10⁻² min⁻¹. This indicates that the antibacterial activity of silver nanorods can be enhanced by applying an electric field, for application in medical and food-preserving fields.

• antibacterial
• silver
• nanorods
• Ti thin film

Acknowledgments

The authors would like to thank the Research Council of Sharif University of Technology for supporting this work. Partial financial support from the Iranian Nanotechnology Initiative is also acknowledged.