Adhesion failure propagation in adhesively-bonded single-lap laminated FRP composite joints

Abstract

This paper deals with three-dimensional non-linear finite element analyses to study the behaviour of embedded adhesion failure propagation in adhesively-bonded single-lap laminated FRP composite joints clamped at one end and subjected to uniform extension at the other end. Because of loading eccentricity and joint material heterogeneity, the embedded adhesion failure is likely to initiate from the stress singularity points and will propagate from either end of the adhesive layer along the adherend–adhesive interfaces. The effects of interaction of such failures and their propagations along the interfaces of the adherends and adhesive are the main concerns of this paper. The peel and shear stresses have been computed along the mid-surface of the adhesive layer for varying adhesion failure lengths to find out the influence of adhesion failure length on the strength of the joint being analyzed. The concept of fracture mechanics has been used to calculate the strain energy release rate (SERR) as the adhesion failure propagates using the virtual crack closure technique (VCCT). It is seen that mode-II SERR is predominant in the propagation of such adhesion failures. The SERR values computed with respect to the adhesion failure lengths being propagated from the two ends of the adhesive layer are seen to be different.

Keywords:

• ADHESION FAILURE
• FRP COMPOSITE
• NON-LINEAR FEA
• SERR
• VCCT