Molecular Recognition-Based Detoxification of Aluminum in Human Plasma

, , , &
Pages 1235-1258 | Published online: 02 Apr 2012
 

Abstract

Molecular recognition-based Al3+-imprinted poly(hydroxyethyl methacrylate-N-methacryloyl-L-glutamic acid) (PHEMAGA–Al3+) beads were prepared to be used in selective removal of Al3+ out of human plasma overdosed with Al3+ cations. The PHEMAGA–Al3+ beads were synthesized by suspension polymerization in the presence of a template–monomer complex (MAGA–Al3+). The specific surface area of PHEMAGA–Al3+ beads was found to be 55.6 m2/g on the average. The MAGA content in the PHEMAGA–Al3+ beads were found to be 640 μmol/g polymer. The template Al3+ cations could be reversibly detached from the matrix to form PHEMAGA–Al3+ using a 50 mM solution of EDTA. The Al3+-free PHEMAGA–Al3+ beads were then exposed to a selective separation procedure of Al3+ out of human plasma, which was implemented in a continuous system by packing the beads into a separation column (10 cm long with an inner diameter of 0.9 cm) equipped with a water jacket to control the temperature. The Al3+ adsorption capacity of the PHEMAGA–Al3+ beads decreased drastically from 0.76 mg/g polymer to 0.22 mg/g polymer as the flow rate was increased from 0.3 ml/min to 1.5 ml/min. The relative selectivity coefficients of the PHEMAGA–Al3+ beads for Al3+/Fe3+, Al3+/Cu2+ and Al3+/Zn2+ were found to be 4.49, 8.95 and 32.44 times greater than those of the non-imprinted PHEMAGA beads, respectively. FT-IR analyses on the synthesized PHEMAGA–Al3+ beads reveals monodentate and bidentate binding modes of Al3+ in complex with the carboxylate groups of the glutamate residues. Density functional theory computations at the B3LYP/6-31G(d,p) basis set suggests that structured water molecules play essential role in the stability of the monodentate binding mode in 1:1 PHEMAGA–Al3+ complexes. The PHEMAGA–Al3+ beads were recovered and reused many times, with no significant decrease in their adsorption capacities.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.