Liquid phase sintering of ferrous powder by carbon and phosphorus control

Abstract

Powder mixtures composed of liquid forming master alloy powder and coarse iron powder were sintered to near full density by having a high amount (20 wt-%) of liquid phase during sintering. This was made possible by the use of the Fe-P-C system with or without Cu. Without post-sintering treatment, a brittle microstructure was obtained. By means of altered C and P control and decarburisation heat treatment of the as sintered material, the final non-brittle microstructure was achieved. Using the open porosity and liquid phase as a diffusion path, rapid decarburisation is created and the local combination of carbon and phosphorus in the microstructure is avoided. In this way, iron phosphide is not formed on grain and/or particle boundaries. Presence of pores is confirmed to be beneficial for grain growth control.