Effects of powder processing on densification of titanium diboride based cermets

Abstract

The sinterability of TiB₂-Ni₃(Al,Ti) based cermets has been significantly improved by aggressive milling of the starting TiB₂-Ni-TiAl₃ powder mixtures. This technique improves not only liquid spreading by reducing TiAl₃ particle size but also eliminates alumina agglomerates and the associated porosity found after vacuum sintering. Liquid phase sintering of TiB₂-Ni-TiAl₃ powder mixtures involves the presence of Ni based secondary borides at low temperatures (1200°C), which react afterwards with TiAl₃ particles leading to the formation of the final TiB₂-Ni₃(Al,Ti) eutectic liquid. Apart from improving liquid spreading around TiB₂ grains, aggressive milling is also found to disperse alumina agglomerates, which reduces the porosity associated to these particles. By this refined procedure, the amount of binder phase required for full densification of TiB₂ cermets by sinter hipping has been reduced from a previous limit of 16 vol.-% to 10 vol.-%. The hardness of these TiB₂-10 vol.-%Ni₃(Al,Ti) cermets is in the range of ultrafine WC-Co hardmetals in spite of their much coarser microstructure.

Keywords:

• POWDER PROCESSING
• DENSIFICATION
• TITANIUM DIBORIDE BASED CERMETS