The microstructure of a multiphase NiAl-33.5Cr-0.5Zr intermetallic alloy was examined by SEM with energy dispersive spectroscopy and TEM. The tensile creep behaviour of the hot isostatically pressed NiAl-33.5Cr-0.5Zr alloy was studied. The results of the creep test indicated that all of the creep curves under the present test have similar characteristics: a short primary creep stage, a dominant tertiary creep stage, and nearly identical creep strains (~45%). The apparent stress exponent and the apparent activation energy were analysed and discussed. The mechanism of the creep deformation was also analysed by the observation of TEM.