Abstract
The non-metallic inclusion content increased significantly when a steel rod of Fe-Ni was remelted by dc electroslag remelting. The silicon content increased slightly. The manganese and sulphur contents did not change. The total aluminium content in the ingot was max. 0·7%, while that in the electrode was only 10 ppm. The aluminium cations Al3+ in the slag are reduced to metallic aluminium at the slag/electrode interface, while O2 - anions are oxidised to dissolved O in the metal pool. This Al and O subsequently recombine to form alumina inclusions in the metal pool. The inclusion content was dependent on the alumina content in the slag. When a rod of plain carbon steel was remelted, however, the increase in nonmetallic inclusion content was as little as one-tenth of that for the remelted Fe-Ni rod. The non-metallic inclusion content was independent of the polarity of the electrode.