Physical properties of selected brazing filler metals

Abstract

A suitable selection of the filler metal is vital for producing satisfactory brazed joints. The wettability of brazing alloys with base metals depends on physical properties such as surface tension, density, melting point, and viscosity. Thermal conductivity and electrical resistivity are also important since the filler metal is frequently required to have similar values to those of the base metal. In the present paper, the physical properties of liquid alloys relevant to brazing have been evaluated. Six different filler metal systems were analysed, comprising alloys based on Ag, Al, Au, Cu, Ni, and Ti. Results show that the viscosity values for most binary brazing filler alloys are of the order of 2–8 mPa s, with Cu and Al alloys exhibiting the lowest viscosities. The surface tensions of brazing alloys vary from 800 to 1800 mN m^-1, with the lowest surface tension values corresponding to the Ag and Al alloys. Thermal conductivity and electrical resistivity values fall in the range 10–200 W m^-1 K^-1 and 17–300 μΩ cm, respectively.

Keywords:

• FILLER METAL
• BRAZED JOINTS
• WETTABILITY
• PHYSICAL PROPERTIES
• SURFACE TENSION
• DENSITY
• MELTING POINT
• VISCOSITY
• THERMAL CONDUCTIVITY
• ELECTRICAL RESISTIVITY
• SILVER BASED ALLOYS
• ALUMINIUM BASED ALLOYS
• GOLD BASED ALLOYS
• COPPER BASED ALLOYS
• NICKEL BASED ALLOYS
• TITANIUM BASED ALLOYS