Effects of Cr, Mn, Si, Cu and Zr on microstructure and mechanical properties of high carbon Fe–16Al alloy

Abstract

Effects of alloying elements Cr, Mn, Si, Cu and Zr on the microstructure and mechanical properties of Fe₃Al (Fe–16Al) based alloy containing ∼0·5 wt-%C have been investigated. Six alloys were prepared by a combination of air induction melting with flux cover and electroslag refining (ESR). ESR ingots were hot forged and hot rolled at 1373 K and were further characterised with respect to microstructure and mechanical properties. The base alloy and the alloys containing Cr, Mn, Si and Cu exhibit a two phase microstructure of Fe₃AlC_0·5 precipitates in Fe₃Al matrix whereas the alloy containing Zr exhibits a three phase microstructure, the additional phase being Zr rich carbide precipitates. Cr and Mn have high solubility in Fe₃AlC_0·5 precipitates as compared to Fe₃Al matrix whereas Cu and Si have very high solubility in Fe₃Al matrix compared to Fe₃AlC_0·5 precipitate and Zr has very low solubility in both Fe₃Al matrix and Fe₃AlC_0·5 precipitate. No significant improvement in room and high temperature (at 873 K) strengths was observed by addition of these alloying elements. Furthermore, it was observed that addition of these alloying elements has resulted in poor room and high temperature ductility. Addition of Cr, Mn, Si and Cu has resulted in marginal improvement in creep life, whereas Zr improved the creep life significantly from 22·3 to 117 h.

Keywords:

• IRON ALUMINIDES
• AIR INDUCTION MELTING
• ELECTROSLAG REMELTING