Abstract
Transient creep of an NiAl hardened austenitic steel was analysed in the temperature range of 823 to 923 K at stresses ranging from 150 to 450 MPa in the frame work of first order reaction kinetics. The present analysis is aimed: to correlate various transient creep parameters with steady state creep rate following first order reaction rate theory to obtain correlation constants; and to arrive at a unified equation to describe primary and steady state regimes of the creep curves in terms of correlation coefficients thus derived. Good correlation of transient creep parameters with steady state creep rate has been obtained over the test conditions studied indicating that the basic mechanism of deformation is the same for all the three stages of creep. Unified equation that fits the experimental creep strain time data for different test conditions over transient and steady state regimes has been obtained in terms of correlation coefficients.