Comparative study of carbon black and graphite powder as carbon source for PM compacts

&
Pages 51-56 | Published online: 19 Jul 2013
 

Abstract

Graphite powder is the most widely used source of carbon in making powder metallurgy components. In this study, the graphite powder was replaced by the nanoscale carbon black powder. Compared to graphite powder, the carbon black powder provides more uniform distribution, higher apparent density, and faster flow rate for the Fe–0·8%C powder mixture. After sintering, the homogenisation of carbon, microstructure, and hardness are all similar between the two carbon powders. But a higher amount of spring back during ejection and thus lower green density was attained by using carbon black powders. Nonetheless, the compacts using carbon black powder had higher amounts of shrinkage, which compensated for the spring back effect during sintering, thus giving the same density as the graphite powder.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.