Effect of MgO addition and sintering parameters on mullite formation through reaction sintering kaolin and alumina

, &
Pages 285-290 | Published online: 18 Jul 2013
 

Abstract

In the present work, the influence of MgO addition and sintering parameters on the formation and densification of mullite was investigated. The morphology of powders and the microstructure of the sintered samples were characterised by means of a scanning electron microscope. X-ray diffraction was used to characterise phases formed in sintered samples. The density of sintered samples was measured using a densimeter and quantified according to the Archimedes principle. MgO was added at 1, 2, 3, 4, 5 and 6 wt-% to kaolin and alumina and the powders were ball milled for 5 h then uniaxially compacted at 75 MPa and finally sintered at 1500, 1550, 1600 and 1650°C for 2, 4, 6 and 8 h. It was found that addition of MgO not only affected mullite formation but also promoted grain growth. For samples containing 0, 1 and 2 wt-%MgO only mullite was formed. While, in addition to mullite, Al2O3 was present in sample containing 3 wt-%MgO. At higher MgO content (4, 5 and 6 wt-%), three phases, i.e. mullite, Al2O3 and spinel, were formed. Addition of 1 wt-%MgO increased the density of all samples for all sintering times and higher densities corresponded to higher sintering temperatures. At higher MgO content, higher temperatures led to lower densities and lower temperatures led to higher densities for almost all sintering times.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.