Abstract
Superpurity aluminum was rolled at 235 and 315°C to 90 per cent reduction in a single pass. The changes in microstructure arising from the deformation were examined by polarized-light and transmission-electron microscopy. The original grains were elongated in the direction of rolling and contained an equiaxed polygonized substructure. The subgrains were larger and more perfect at the higher rolling temperature. The extent of dynamic recovery is compared with that of commercial-purity aluminum and with that of other face-centred cubic metals.
Résumé
Un taux de réduction de 90% par laminage en une seule opération a été effectué sur de l'aluminium à 99.99% de pureté à 235 et à 315°C. Les modifications de la structure dues à cette déformation ont été éxaminées en lumière polarisée et par microscopie électronique en transmission. Les grains originaux sont allongés dans le sens de la déformation et présentent une sous-structure polygonalisée équiaxiale. Des sous-grains plus réguliers et plus gros ont été obtenus à la température la plus élevée. L'importance de la restauration dynamique est comparée avec celle de l'aluminium de pureté commerciale et avec celie d'autres métaux cubiques à faces centrées.