Abstract
Data from the literature were used to construct activity diagrams for the systems Mn–Fe–C, MnO–CaO–SiO2 and CaO–Al2O3–SiO2 with 10% MnO. Assuming that the reduction temperature is close to slag melting point, the MnO content required to obtain a 75% Mn alloy can be found. One can also calculate the Si content corresponding to the slag composition. Fixing the allowable %Si it is found that the slag will contain more than 25% MnO in the MnO–CaO–SiO2 system. The effect of CO pressure is minor. If it is practical to add Al2O3 to the slag, its melting point can be lowered sufficiently to obtain slags with 10% MnO in the CaO–Al2O3–SiO2 system while keeping Si in the metal low.
Résumé
Des données de la littérature ont été employées pour construire les diagrammes d'activité des systèmes Mn–Fe–C, MnO–CaO–SiO2, et CaO–Al2O3–SiO2 it 10% de MnO. En admettant que la température de la zone de réduction est proche de celle de fusion du laitier, on trouve la teneur en MnO nécessaire pour obtenir l'alliage à 75% de Mn. La quantité de Si réduit a également été déterminée. Le calcul montre qu'en fixant la teneur finale silicium à moins de 0.5% la teneur en MnO doit être supérieure à 25% . dans les laitiers MnO–CaO–SiO2. La pression de CO n'a guere d'effet. S'il est pratique d'ajouter du Al2O3 au laitier pour en abaisser le point de fusion on peut obtenir avec un laiter it 10 % de MnO un alliage pour lequelle Si ne dépasse pas les bornes permises.