Abstract
From an analysis of the local atomic arrangement in ordered γ′-particles it is deduced that the effect of dislocation splitting on the critical resolved shear stress of γ′-hardened materials is very small. This result is in striking contrast to the ones obtained for lattice misfit and modulus hardening.
MST/146