The formation and growth of voids on the grain boundaries of a Nimonic 105 superalloy subjected to high temperature and stress has been followed using small-angle neutron scattering. The size of the voids increases with treatment time and is well correlated with the creep. The volume and surface fractions of the voids are evaluated.