Compacts of chromium oxide/chromium mixtures have been sintered in vacuum at temperatures up to 1600°C to produce cermets. Two types of chromium powder were used—an electrolytic and an aluminothermic powder. The effect of chromium content and of sintering temperature on the sintered density and microstructure has been studied and supplemented by tests of hardness and compressive strength.
Considerable densification was achieved by additions of chromium in the range 1–50 wt.-%, with the optimum content at 5–10%. Compressive strengths < 10 tons/in2 were attained over a wide range of composition.