Evaporation Behavior of Hastelloy-X Alloys in Simulated Very High Temperature Reactor Environments

Abstract

A sequential analysis was made on the material degradations during exposure of nickel-base corrosion-resistant austenitic alloys to simulated very high temperature reactor environments. The materials tested were two modified versions of Hastelloy-X in terms of both increased manganese content for improved compatibility and decreased manganese content for possible adverse effects. Quantitative analysis of the specimens after exposure for 1000 h at several temperature steps from 850 to 1050°C have revealed the temperature-dependent aspects of the processes including the depletion of chromium and manganese due to oxidation, evaporation, and carbon transfer into and/or from the materials. The material with enriched manganese, developed and specified as Hastelloy-XR, showed enhanced resistance to loss of chromium in terms of both oxidation and evaporation.