Abstract
Objective
The purpose of this study was to assess the hardness, mineral content, surface roughness, and micromorphology of sound and slightly demineralized enamels, before and after bleaching procedure using 10% carbamide peroxide.
Methods
Sixty bovine dental blocks were randomly divided into the following two groups: 30 slabs were submitted to three cycles of pH and 30 slabs were noncycled. Hardness (n=10) was measured using the microhardness tester with Knoop indenter under a 50 g load for 5 seconds. The calcium/phosphate (Ca/P) ratio (n=10) was obtained using a micro-energy-dispersive X-ray fluorescence (μ-EDXRF) spectrometer. The measurement of roughness average (n=10) was performed using a surface roughness tester. Specimens were bleached 6 hours/day during 21 days, and then, physicochemical properties were re-evaluated. Two additional specimens were carried out to evaluate surface micromorphology using the scanning electron microscopy. Data were statistically analyzed by ANOVA and Tukey’s test (α=0.05).
Results
Sound and slightly demineralized enamels showed no difference in Ca/P ratio after dental bleaching according to the μ-EDXRF analysis, but the Ca/P ratio decreased after bleaching for slightly demineralized enamel. Bleaching treatment decreased the hardness and increased the surface roughness, causing micromorphology alterations.
Conclusion
Therefore, bleaching procedure promoted change in bovine enamel surface and increased the demineralization of slightly demineralized enamel but not affected the mineral content of sound enamel.
Disclosure
The authors report no conflicts of interest in this work.