Abstract
Purpose: To assess the potential impact of corneal crosslinking treatment (365 nm ultraviolet (UV)A irradiation with riboflavin) on the material properties of Intracorneal Rings Segments (ICRS).
Materials and methods: Material properties were studied using FT-IR spectroscopy and UV-Vis spectroscopy. Rings were examined: (1) after installation of riboflavin solution, (2) after irradiation with UV-A light and (3) after instillation of riboflavin solution followed by instillation and coeval irradiation. The experiments followed the standard corneal cross-linking (CXL) protocol of corneal crosslinking treatment.
Results: After instillation of riboflavin solution, a permanent intense yellow staining of the samples was observed. UV-Vis spectroscopy confirmed that a certain amount of riboflavin solution was absorbed into the samples after CXL procedure. FT-IR spectroscopic analysis showed alterations in the spectra of ICRS mainly at the 2800–3200 cm−1 spectral region [modification in band intensities of CH2 (2925 cm−1) and CH3 (2950 cm−1)].
Conclusions: Our results suggest crosslinking reaction in ICRS material. This should be taken into consideration prior to any CXL treatment of post ICRS-implanted cornea.
Declaration of interest
The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.