Electrochemical Properties of MgZnCa-Based Thin Film Metallic Glasses Fabricated by Magnetron Sputtering Deposition Coated on a Stainless Steel Substrate

, , , , &
Pages 1588-1602 | Received 27 Jul 2020, Accepted 24 Aug 2020, Published online: 03 Sep 2020
 

Abstract

Steels are majorly used for diverse structural applications; however, they suffer severe degradation in a corrosive environment which necessitates the need for a protective surface coating. In this paper, the electrochemical study of MgZnCa alloy thin film coating on an AISI 304 stainless steel was reported. The study intends to investigate the influence of coating thickness on the electrochemical performance of the ternary MgZnCa alloy thin film. The polarization results indicated that better corrosion resistance is achieved when the MgZnCa coating is applied on the steel substrate, as the corrosion current density of the 4 µm coating (0.28 mA/cm2) is lower than for the uncoated substrate (0.44 mA/cm2). As the MgZnCa coating thickness increases from 4 to 6 µm, a decrease in the corrosion density with a resultant increase in the corrosion potential was observed. The microstructural characterization revealed fewer corrosion attacks for the coated substrates as compared with the uncoated material with the presence of more degradation products. The corrosion resistance of the steel substrate is enhanced by the application of MgZnCa coating and increasing coating thickness is significantly beneficial.

Additional information

Funding

T.O. Olugbade acknowledges the support of the research grant council (RGC), Hong Kong PhD Fellowship Scheme (PF16-02783), Hong Kong SAR, China.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 768.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.