Abstract
In this study, a novel biopolymer based on poly(glycerol sebacic)-urethane (PGS-U) and its nanocomposites containing Cloisite@30B were synthesized by facile approach in which the crosslinking was created by aliphatic hexamethylene diisocyanate (HDI) at room temperature and 80 °C. Moreover, metronidazole and tetracycline drugs were selected as target drugs and loaded into PGSU based nanocomposites. A uniform and continuous microstructure with smooth surface is observed in the case of pristine PGS-U sample. The continuity of microstructure is observed in the case of all bionanocomposites. XRD result confirmed an intercalated morphology for PGSU containing 5 wt% of clay nanoparticles with a d-spacing 3.4 nm. The increment of nanoclay content up to 5%, the ultimate tensile stress and elastic modulus were obtained nearly 0.32 and 0.83 MPa, which the latter was more than eight-fold than that of pristine PGS-U. A sustained release for both dugs was observed by 200 h. The slowest and controlled drug release rate was determined in the case of PGSU containing 5 wt% clay and cured at 80 °C. A non-Fickian diffusion can be concluded in the case of tetracycline release via PGS-U/nanoclay bionanocomposites, while a Fickian process was detected in the case of metronidazole release by PGS-U/nanoclay bionanocomposites. As a result, the designed scaffold showed high flexibility, which makes it an appropriate option for utilization in the treatment of periodontal disease.
GRAPHICAL ABSTRACT
![](/cms/asset/3b89b842-bd57-4b0c-bdd5-f465cfb59138/tbsp_a_1992588_uf0001.jpg)
Disclosure statement
No potential conflict of interest was reported by the author(s).
Funding
The author(s) reported there is no funding associated with the work featured in this article.