The effect of long-term oxidation on the total hemispherical emissivity of Type 316L stainless steel (SS 316L) is of interest in nuclear plant safety and is reported on here. ASTM standard C835-06 [American Society for Testing and Materials, 2006] was used for measuring the total hemispherical emissivity of this material for the following surface conditions: (1) “as-received” from the manufacturer (essentially unoxidized) and (2) oxidized in air at 573 K for up to 3000 h. The emissivity of the as-received samples varied within the range from 0.24 at 434 K to 0.34 at 1026 K. Oxidation in air at 573 K for 500 h increased the emissivity range of the oxidized sample from 0.28 at 429 K to 0.38 at 1096 K. There was no further significant change in emissivity observed following an increase in the oxidation time from 500 to 3000 h. It is suspected that the emissivity ceased to increase during the additional oxidation time because of chromium oxide that formed on the SS 316L surface inhibiting further oxidation.
Acknowledgments
This research was supported by the U.S. Department of Energy through grant NEUP-5252. Support for F. Al Zubaidi was provided by the Ministry of Higher Education and Scientific Research, Technology University, Iraq. K. L. Walton has been partially supported through U.S. Nuclear Regulatory Commission fellowships and U.S. Department of Education Graduate Assistance in Areas of National Need fellowships.