Synthesis and characterization of castor oil-based polyols with fluorine-containing pendant groups

Abstract

A novel castor oil-based polyols with fluorine-containing pendant groups (CO-FPOL) has been synthesized through ring-opening polymerization from castor oil (CO), propylene oxide (PO) and self-made 3-(3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoro-octyloxymethyl)-Oxirane (TDFOMO). The TDFOMO was synthesized from 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoro-1-octanol (TDFOL) and Epichlorohydrin (ECH). Then, the CO-FPOLs further reacted with a 4,4′-diphenylmethane diisocyanate (MDI) to prepare a one-component fluorinated polyurethane coating (CO-FPUP). Strikingly, the fluorine content of CO-FPOL can be easily controlled, the thermal stability of CO-FPOL and CO-FPUP increased with the increasing of fluorine content. It was all found that with the fluorine content of CO-FPOL increasing from 0% to 17.72%, the static water contact angle of CO-FPUPs increased from 90° to 106°, and the static oil contact angle of CO-FPUPs increased from 20° to 54°. The XPS survey spectra revealed that the fluorine in the cured polyurethane would migrate to the surface easier due to the fluorinated pendant groups which moving easier between molecular chains. All the above results suggest that the introduction of fluorinated pendant groups in polyether polyol has great improvements in the thermal stability and the hydrophobic and oleophobic properties of polymer materials.

Keywords:

• Castor oil-based polyols
• fluorinated polyether polyol
• oleophobic
• hydrophobic
• polyurethane

Acknowledgments

We would like to thank the financial support from the Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions, China. The test supports from the teachers of Advanced Analysis & Testing Center of Nanjing Forestry University are also greatly appreciated.

Disclosure statement

No potential conflict of interest was reported by the author(s).