Formation and structure of chitosan–poly(sodium methacrylate) complex nanoparticles

ABSTRACT

Interpolyelectrolyte complex (IPEC) dispersions were prepared from chitosan and poly(sodium acrylate), NaPMA, by mixing their solutions, at different carboxyl-to-aminium molar ratios, r_CA. Gyration radius was determined by small angle x-ray scattering (SAXS) and showed that, as r_CA was increased, IPEC dimensions decreased and reached a minimum at r_CA = 0.75, which was considered the ratio at which IPEC cluster dimensions were minimum, following collapse, phase segregation, nucleation, and growth of larger particles. Pair distance distributions, P(r), became narrower up to r_CA = 0.75, increasing its width from this point. Relaxation-related parameters from dynamic light scattering (DLS) intensity correlation functions (ICFs) identified three main relaxation processes. The fast process, related to free polyelectrolyte molecules random motion disappeared as r_CA, was increased. The other two relaxation processes also were a function of r_CA and presented marked changes at r_CA = 0.75. At the same value of r_CA, the energy of activation for the average relaxation rate showed the occurrence of a clear change in the nature of IPEC-related interactions. As hydrodynamic diameter, determined by DLS, was much larger than the gyration radius determined by SAXS, IPEC particles could be described as being composed by a core, rich in segregated, insoluble material, enveloped by IPEC soluble clusters, possibly in the form of water-rich gels.

GRAPHICAL ABSTRACT

KEYWORDS:

• Chitosan
• DLS
• interpolyelectrolyte complex
• IPEC
• PEC
• polyelectrolyte complex
• SAXS