Strain-induced martensite reversion in 18Cr–8Ni steel – transmission Kikuchi diffraction study

ABSTRACT

Reverse transformation of strain-induced martensite (SIM) was studied in the 18Cr–8Ni stainless steel. Microstructure analysis was performed on samples in an as-deformed state and after reversion annealing at 873 and 973 K, using the transmission Kikuchi diffraction. The primary, as well as reversed, austenite possesses the Kurdjumov–Sachs crystallographic orientation relationship, with respect to the SIM. The reverted austenite keeps one orientation within all reverted grains, regardless of the applied heating procedure, where the amount of reverted austenite depends only on the annealing temperature.

KEYWORDS:

• Transmission Kikuchi diffraction
• electron microscopy
• phase transformation
• orientation imaging microscopy
• austenitic stainless steel
• strain-induced martensite

Disclosure statement

No potential conflict of interest was reported by the authors.

ORCID

G. Cios http://orcid.org/0000-0003-4269-5456

Additional information

Funding

This work was supported by the Polish National Science Centre (Narodowe Centrum Nauki, NCN) [grant number 2016/23/N/ST8/01252].