Figures & data
FIG. 1 (a) XRD of AgNi particles, composed of 60 at% Ag and 40 at% Ni and generated at 1000°C; (b) backscatter SEM images of AgNi particles; (c) EDS mapping of AgNi particles; (d) XRD of CuNi particles, which were composed of 60 at% Cu and 40 at% Ni and generated at 1000°C; (e) SEM images of CuNi particles; (f) EDS mapping of CuNi particles; (g) XRD of AgCu particles, composed of 60 at% Ag and 40 at% Cu and generated at 1000°C; (h) backscatter SEM images of AgCu particles with inserted SEM images of particles with Cu solid solution removed; and (i) EDS mapping of AgCu particles. (Color figure available online.)
FIG. 2(a) SEM images of AgCu particles, which were composed of 60 at% Ag and 40 at% Cu and generated at 750°C. A 2.5 L/min N2 was used as carrier gas. (b) Backscatter SEM images of AgCu. Particles were composed of 40 at% Ag and 60 at% cu and generated at 750°C. 2.5 L/min N2 was used as carrier gas. (Color figure available online.)