Bentonite (Bt) with irregular shape and surface morphology was used as a new type of filler in EPDM. EPDM/Bt composites were prepared using a laboratory size two-roll mill by adding 0 to 70 phr Bt. The effects of Bt loading on curing characteristics, morphology, tensile and thermal properties of EPDM/Bt composite were studied. Scorch and curing time were decreased with 0 to 30 phr loading and increased subsequently at 50 and 70 phr. Tensile strength and elongation at break (Eb) were increased with increasing Bt loading from 0 to 50 phr and decreased at 70 phr, whereas the tensile modulus (M100%) shows an increasing trend with increasing Bt loading. Thermogravimetric analysis shows the enhancements of thermal properties with increasing Bt loading. Morphological studies of tensile fracture surfaces of EPDM/Bt composite proves good interaction between Bt particles and EPDM at 50 phr and formation of Bt agglomerates at 70 phr.
ACKNOWLEDGMENT
The author (M. Mathialagan) would like to thank Universiti Sains Malaysia for the financial support under USM fellowship scheme for his MSc study.