Abstract
Homo-crystallization and melting behavior of poly(L-lactic acid) (PLLA) with poly(D-lactic acid) (PDLA) (≤10 wt.%) was studied. The different thermal history had been applied to exert structural variation on stereocomplex (SC). The PLLA/PDLA blend showed different crystallization and melting behavior when cooled from 250°C or 200°C. Double melting peaks were observed after the blend was cooled from 250°C. SC annealing at different temperatures exhibited significant effect for melt-crystallization of PLLA. Influence of initial melting condition before cooling was also investigated. The cold crystallization of amorphous blend initially was studied and some novel results had been observed.