ABSTRACT
In this paper, the remaining creep life of SA-304L stainless steel at elevated temperatures is studied. The small punch creep tests (SPCT) were performed on SA-304L virgin and aged materials at constant loads. Times to fracture and the minimum deflection rate in SPCTs were recorded, and the time-temperature parametric analysis was performed, based on experimental results. The constants of the Larson–Miller parameter and the Monkman–Grant relationship were obtained for different consumed creep life ratios, and eventually the equations were established to explain the variation of constants of the Larson–Miller parameter and the Monkman-Grant relationship with respect to the consumed creep life ratio.