Influence of Sliding Speed on the Tribological Characteristics of Si₃N₄-hBN Ceramic Materials

Abstract

The influence of sliding speed on the unlubricated tribological behaviors of silicon nitride–boron nitride (Si₃N₄-hBN) composites was investigated with two modes in air by a pin-on-disc tribometer. Using the upper disc–on–bottom pin test mode, as the sliding speed increased, the friction coefficient of the sliding pairs showed an upward trend; for example, from 0.18 at the sliding speed of 0.40 m/s to 0.54 at the sliding speed of 1.31 m/s for the Si₃N₄/Si₃N₄–20% hBN pair. The surface analysis indicated that a tribochemical film consisting of SiO₂ and H₃BO₃ formed on the wear surfaces of the Si3N4/Si3N4–20% hBN sliding pair at sliding speeds of 0.40 and 0.66 m/s. Moreover, the formation of this film lubricated the wear surfaces. At the sliding speed of 1.31 m/s, no tribochemical film formed on the wear surfaces, most likely due to the increase in surface temperature. In the upper pin–on–bottom disc test mode, the wear mechanism was dominated by abrasive wear, and no tribochemical products could be detected on the wear surfaces. The increase in sliding speed weakened the degree of abrasive wear, leading to a decrease in the friction coefficients.

KEY WORDS:

• Composite Ceramics
• Unlubricated Wear
• Sliding Speed
• Boric Acid

ACKNOWLEDGEMENTS

The authors thank the Natural Science Foundation of China (No. 50672074) and Scientific Research Starting Foundation for Introducing Doctor of Shaanxi University of Science & Technology (BJ11-01).