A comparative study of gamma radiation effects on track properties of different PADC detectors

Abstract

Track properties of gamma-irradiated polyallyldiglycol carbonate (PADC) detectors (Homalite, Pershore and Trastrack) are studied in the dose range of 10¹–10⁶ Gy. Results show that the bulk and track etch rates of all three types of PADC detector increase at doses higher than 10⁴ Gy. This increase is more pronounced in post-gamma exposed detectors. The change in etch rate ratio (S) for post-gamma exposed PADC–Homalite detectors is more significant when compared with the other detectors. The critical angle for etching shows that etching at a low temperature of 60 °C is more effective, and the critical angle value is decreased to a significant extent for all three types of PADC detectors. Etching efficiency of post-gamma exposed samples is found to be much higher than the pre-gamma exposed sample at the highest dose of 10⁶ Gy. When compared, it was found that of the three PADC detectors, PADC–Homalite detectors seem to be more sensitive to gamma irradiation.

Keywords:

• polyallyldiglycol carbonate
• gamma dose
• etch rates
• pre-gamma
• post-gamma

Acknowledgements

This paper is dedicated to Professor K.K. Dwivedi, DST, Government of India, for having introduced the author to this area of research. Support under DST-FIST is greatly acknowledged.