Effect of Annealing on Virgin and Recycled Carbon Fiber Electrochemically Deposited with N-type Bismuth Telluride and Bismuth Sulfide

Abstract

N-type thermoelectric bismuth telluride (Bi₂Te₃) and bismuth sulfide (Bi₂S₃) were deposited on virgin carbon fiber (VCF) and recycled carbon fiber (RCF) substrates by electrodeposition. The effects of annealing on the surface morphology and the Seebeck coefficient of the Bi₂Te₃ and Bi₂S₃ films were investigated. A nearly stoichiometric N-type Bi₂Te₃ was obtained from an electrolyte solution of 8 mM of Bi(NO₃)₃.5H₂O and 10 mM of TeO₂, which displayed the highest Seebeck coefficient of −20.01 and −13.0 µV/K for VCF and RCF, respectively. The deposition of Bi₂S₃ was slightly off-stoichiometry, but the improvement was still significant with a Seebeck coefficient of −16.3 and −12.4 µV/K for VCF and RCF, respectively. The effect of varying the annealing temperature (275°C and 350°C) and annealing time (2 and 3 hours) was studied on a nearly stoichiometric N-type Bi₂Te₃. The result shows an improvement in the Seebeck coefficient by 1.51–1.24 times at 350°C for 2 hours.

Keywords:

• Annealing
• Bismuth sulfide
• Bismuth telluride
• Recycled carbon fiber (RCF)
• Seebeck coefficient
• Thermoelectricity
• Virgin carbon fiber (VCF)