Fabrication of composites from different carbon content ferrous powders adopting thermomechanical processes

ABSTRACT

In this research, deep consolidation technique is utilized for processing of low and high carbon content ferrous powders to manufacture composite material. High carbon content ferrous powders were used as reinforcing material. The powder particles were allowed to mix with low carbon content ferrous powders in 50:50 weight percent for fabrication of composites. The composites were heat treated at three different temperatures (i.e., 800°C, 900°C, and 1000°C). The changes in microstructure, microhardness, the grain size, and bonding among powder particles were studied. Refinement of grains was observed and this led to improved hardness enabling the processed material to be used as a suitable composite. Abrasive wear tests were carried out using a laboratory tribometer in dry reciprocating sliding contact against Sic abrasive paper. The outcomes demonstrate that the abrasive wear resistance was notably affected by the treatment temperature and hardness of the composites.

KEYWORDS:

• Ferrous powder
• pressing
• hot-forging
• rolling
• heat-treatment
• microhardness
• abrasive wear
• SEM