Abstract
Sr2Bi4−x Dy x Ti5O18 (SBDT-x, x = 0–0.20) ceramic samples were prepared, and their dielectric and ferroelectric properties were measured. The remnant polarization (2P r ) of SBDT-x increased at first, then decreased with the increase of Dy content. When Dy content was 0.01, the 2P r reached a maximum value of 20.1 μC · cm−2. The variation of 2P r for SBDT-x related to space charge density and structure distortion. The coercive field (E c ) increased a little after doping. The E c of SBDT-0.01 was 44.2 kV · cm− 1. The ferroelectric property of Sr2Bi4Ti5O18 was enhanced by Dy doping with appropriate content.