Structural and Electrical Properties of Ba(Zr_xTi_1-x)O₃ Films Prepared by RF-magnetron Sputtering Using Metal Targets

Abstract

Ba(Zr_xTi_1-x)O₃ (BZT) thin films with different Zr contents were deposited on (100)MgO and (100)Pt/(100)MgO substrates by RF-magnetron sputtering using metal targets. The BZT thin films had a single perovskite phase with only (001)/(100) orientation. In all cases, the ratio of Ba/Ti was stoichiometry and BZT films possess a dense microstructure. The grain size was decreased and BZT thin films showed ferroelectric-to-paraelectric properties with increasing Zr content. At room temperature, the tunability of nearly 30% was achieved at 1 MHz; meanwhile, a relatively low dielectric loss was obtained. These results indicated that we succeeded in depositing high-quality and potential tunable ferroelectrics.

Keywords:

• BZT films
• reactive sputtering
• metal targets
• grain size
• tunability