Melamine modified polyester amide (MPEA) was synthesized by the reaction of linseed oil fatty amide. The resin was further cured at room temperature by polystyrene co‐maleic anhydride (SMA) in different phr (30–80) to obtain MPEA coatings. The probable structure of MPEA was confirmed by FT‐IR, 1H‐NMR and 13C‐NMR spectroscopic techniques. The physico‐chemical characterization of these resins viz. iodine value, saponification value, refractive index, inherent viscosity were carried out by standard methods. MPEA (40 wt%) solution in ethylene glycol monomethyl ether (EGME) was applied on a mild steel strip of standard sizes to study their physico‐mechanical and chemical resistance properties. It was found that coatings of MPEA with 60 parts per hundred of the resin (phr) of SMA showed the best performance in physico‐mechanical and alkali resistance properties. Thermal stability and curing behavior were studied by Thermo Gravimetric Analyses (TGA) and Differential Scanning Calorimetry (DSC), respectively.
Studies on Melamine Modified Polyesteramide as Anticorrosive Coatings from Linseed Oil: A Sustainable Resource
Log in via your institution
Log in to Taylor & Francis Online
Restore content access
Restore content access for purchases made as guestPDF download + Online access
- 48 hours access to article PDF & online version
- Article PDF can be downloaded
- Article PDF can be printed
Issue Purchase
- 30 days online access to complete issue
- Article PDFs can be downloaded
- Article PDFs can be printed
Related Research
People also read lists articles that other readers of this article have read.
Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.
Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.