Two novel diamine monomers, bis(4‐amino‐3,5‐dimethylphenyl)‐3‐pyridyl methane and bis(4‐aminophenoxy‐3,5‐dimethylphenyl)‐3‐pyridyl methane were synthesized. A series of pyridine containing aromatic polyimides derived from the diamines were synthesized through a typical two‐step polymerization method. Most of the polymers show good solubility in NMP, DMAc, DMF, DMSO and CHCl3 at room temperature. These polyimides exhibit Tg in the range of 249–317°C and 10% wt loss (T10) takes place in the range of 474–564°C in N2 and 469–558°C in air. The polymers have tensile strength in the range of 88–96 MPa, elongation at break in the range of 8.5–12.5% and tensile modulus in the range of 1.5–2.1 GPa. These polyimides also have low dielectric constant (3.26–3.64 at 1 KHz and 3.24–3.61 at 10 KHz) and low moisture absorption (0.42–0.89%).
Synthesis and Characterization of Organosoluble Polyimides Containing Pyridyl Moiety with Ether Linkages
Log in via your institution
Log in to Taylor & Francis Online
Restore content access
Restore content access for purchases made as guestPDF download + Online access
- 48 hours access to article PDF & online version
- Article PDF can be downloaded
- Article PDF can be printed
Issue Purchase
- 30 days online access to complete issue
- Article PDFs can be downloaded
- Article PDFs can be printed
Related Research
People also read lists articles that other readers of this article have read.
Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.
Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.