Synthesis and characterization of thermally stable poly(ether-azomethine)s derived from 1,1-bis[4-(4-benzaldehyde oxy)-3-methyl phenyl] cyclopentane

ABSTRACT

A new dialdehyde 1,1-bis[4-(4-benzaldehyde oxy)-3-methyl phenyl] cyclopentane (BBMPC) was synthesized starting from cyclopentanone and O-cresol to give 1,1-bis(4-hydroxy-3-methyl phenyl)cyclopentane (BHMPC); followed by reaction with 4-fluorobenzaldehyde in N, N-dimethyl formamide (DMF), containing anhydrous potassium carbonate. New series of poly(ether-azomethine)s were synthesized from (BBMPC) with different diamines such as 4,4′- diamino diphenyl ether (ODA); 4,4′-diaminodiphenyl methane (MDA); 4-aminophenyl sulfone (SDA); p-phenylene diamines (p-PDA), etc. in N, N’- dimethyl acetamide (DMAc) with 5 wt% LiCl by the solution polycondensation method. Inherent viscosities of these polymers were in the range 0.20 to 0.38 dL/g indicating formation of moderate molecular weights. These polymers exhibited good solubility in various polar aprotic solvents such as N-methyl-2-pyrrolidone (NMP), DMAc, DMF, etc. However some polymers showed partial solubility in DMF and DMAc. X-Ray diffraction pattern of polymers showed amorphous nature. Thermal stability was assessed by 10% weight loss temperature and the degradation temperature of the resultant polymers falls in the ranges from 444-501°C in nitrogen. The glass transition temperature was in the range of 155-205°C. The structure-property correlation among these polyazomethines were studied; in view of their potential applications as high performance polymers.

KEYWORDS:

• 1,1-Bis[4-(4-benzaldehyde oxy)-3-methyl phenyl] cyclopentane
• cardopoly(ether-azomethine)s
• glass transition temperature thermal properties

Acknowledgments

The authors are thankful to the Scientific Instrumentation Center, Solapur University for consistent analysis of samples.