Surface modification of layered silicates. II. Factors affecting thermal stability

Abstract

Different aluminosilicates, such as montmorillonite, vermiculite and mica, were surface-treated with a variety of organic modifiers to quantify factors affecting the thermal stability of the modified fillers. Montmorillonites with different cation exchange capacities were also used. Thermal characterisation was carried out via high resolution thermogravimetric analysis and the results were correlated with X-ray diffraction measurements. Modified substrates, such as montmorillonite, vermiculite and mica, differed in their thermal behaviour even when modified with the same surface modifiers. Phosphonium-based modifiers were the most thermally stable, compared to pyridinium and ammonium ions. Mixed brushes from the modifiers also influenced the thermal behaviour of the modified substrates. When further modified using physical adsorption or chemical reactions on the surface, the modified minerals also displayed alterations in the thermal behaviour of the fillers. The results can be used as a guide for the selection of surface modifiers in the nanocomposite synthesis process where compounding of the filler with the polymer at high temperature and shear is required.

Keywords:

• thermal behaviour
• montmorillonite
• cation exchange capacity
• mica
• vermiculite
• organo-clay

Acknowledgements

The experimental work was carried out at the Institute of Chemical and Bioengineering, Department of Chemistry and Applied Biosciences, ETH Zurich, Switzerland.