Figures & data
Figure 1. HAADF-STEM images of (a) Au 1.0/Pd 0, (b) Au 0.75/Pd 0.25, (c) Au 0.50/Pd 0.50, (d) Au 0.25/Pd 0.75 and (e) Au 0/Pd 1.0 bimetallic NP-immobilised TiO2.
![Figure 1. HAADF-STEM images of (a) Au 1.0/Pd 0, (b) Au 0.75/Pd 0.25, (c) Au 0.50/Pd 0.50, (d) Au 0.25/Pd 0.75 and (e) Au 0/Pd 1.0 bimetallic NP-immobilised TiO2.](/cms/asset/fbb28ce4-5954-49ff-bb94-bb8dac25a35e/tjen_a_824617_f0001_b.gif)
Table 1. Structures of immobilised Au/Pd bimetallic NPs. Insets are the image intensity profiles along the indicated lines.
Figure 2. (a) IR spectra of CO adsorbed on Au/Pd bimetallic NP-immobilised TiO2 and (b) the relationship between the surface areas of the immobilised NPs and the peak areas of adsorbed CO.
![Figure 2. (a) IR spectra of CO adsorbed on Au/Pd bimetallic NP-immobilised TiO2 and (b) the relationship between the surface areas of the immobilised NPs and the peak areas of adsorbed CO.](/cms/asset/ac8670e2-5d1c-44e9-9e27-b01896fa1fb2/tjen_a_824617_f0002_b.gif)
Figure 3. TOF (per Au + Pd) of (a) Au-core/Pd-shell bimetallic NPs and (b) mixture of monometallic Au and Pd NP-immobilised TiO2 (left axis) and (c) synergistic factor (histogram, right axis).
![Figure 3. TOF (per Au + Pd) of (a) Au-core/Pd-shell bimetallic NPs and (b) mixture of monometallic Au and Pd NP-immobilised TiO2 (left axis) and (c) synergistic factor (histogram, right axis).](/cms/asset/e3ebc75b-ea25-434c-9691-9deaf7ac43d9/tjen_a_824617_f0003_b.gif)
Figure 4. Catalytic activities normalised by the surface area of immobilised (a) Au-core/Pd-shell bimetallic NPs and (b) mixture of monometallic Au and Pd NPs.
![Figure 4. Catalytic activities normalised by the surface area of immobilised (a) Au-core/Pd-shell bimetallic NPs and (b) mixture of monometallic Au and Pd NPs.](/cms/asset/4de2fef3-6c39-47e7-9415-cf0331237d05/tjen_a_824617_f0004_b.gif)
Figure 5. (a) Pd 3d and (b) Au 4f XPS spectra of Au-core/Pd-shell bimetallic NPs immobilised on TiO2.
![Figure 5. (a) Pd 3d and (b) Au 4f XPS spectra of Au-core/Pd-shell bimetallic NPs immobilised on TiO2.](/cms/asset/95b0a2fc-21da-4344-8879-bf5b141cd4c7/tjen_a_824617_f0005_b.gif)
Table 2. HAADF-STEM images and the sizes of TiO2 immobilising Au/Pd bimetallic NPs prepared from 0.25 mM HAuCl4 and various concentrations of Na2PdCl4.