Shear fracture characterization of green-glued polyurethane wood adhesive bonds at various moisture and gluing conditions

Abstract

The shear fracture properties of green-glued one-component polyurethane (PUR) wood adhesive bonds subjected to kiln drying were investigated. The local shear strength and fracture energy of the wood adhesive bonds were determined from experimentally recorded complete shear stress versus deformation curves of the bond line. A stable test set-up and small specimens that were anti-symmetrically loaded were used in order to get a uniform and pure state of shear stress. Different moisture contents (MCs) and pressing times were investigated. The fracture properties of conventionally dry-glued wood adhesive bonds and of solid wood were used as reference. The results show that the fracture energy of green-glued bonds with PUR adhesive is dependent on the MC of wood and on the pressing time. The same fracture energy and strength can be obtained by green gluing as by dry gluing, but there seems to exist a maximum MC of sapwood, in the range between 78% and 160%, and a minimum pressing time, in the range between 3 h and 48 h, for which it can be achieved. Both dry- and green-glued polyurethane adhesive bonds were more ductile than solid wood.

Keywords:

• Green gluing
• fracture energy
• shear strength
• wood
• adhesive bonds
• stress versus deformation

Acknowledgements

This work was supported by The Knowledge Foundation (the KK Foundation) and Frans and Carl Kempe's Foundation, both Sweden.