Figures & data
Figure 2. Typical SEM image of a fracture surface of a HPed (Cr,Mn)2AlC sample with an initial Cr:Mn ratio of 1.8:0.2 at (a) low magnification and (b) higher magnification. Kinking and delamination of MAX phase grains are obvious in (b).
![Figure 2. Typical SEM image of a fracture surface of a HPed (Cr,Mn)2AlC sample with an initial Cr:Mn ratio of 1.8:0.2 at (a) low magnification and (b) higher magnification. Kinking and delamination of MAX phase grains are obvious in (b).](/cms/asset/7dd15249-3c2d-4cea-aa04-77c0987440e8/tmrl_a_944676_f0002_b.gif)
Figure 3. Characteristic nanolaminated structure of (a) (Cr,Mn)2AlC and, (b) (Cr,Mn)2GaC; (c) and (d) SAED patterns along the [11¯00] and [112¯0] zone axis, respectively, in (Cr,Mn)2GaC.
![Figure 3. Characteristic nanolaminated structure of (a) (Cr,Mn)2AlC and, (b) (Cr,Mn)2GaC; (c) and (d) SAED patterns along the [11¯00] and [112¯0] zone axis, respectively, in (Cr,Mn)2GaC.](/cms/asset/663f87bf-6477-4e56-a42d-37b9a618aed7/tmrl_a_944676_f0003_b.gif)
Figure 4. XRD θ–2θ scans of (a) (Cr,Mn)2GaC sample with a Cr:Mn ratio of 1:1 in the initial powder and, (b) HCl treated (Cr,Mn)2GaC sample.
![Figure 4. XRD θ–2θ scans of (a) (Cr,Mn)2GaC sample with a Cr:Mn ratio of 1:1 in the initial powder and, (b) HCl treated (Cr,Mn)2GaC sample.](/cms/asset/27e213e7-7283-4eec-ba64-1aaa33e0debd/tmrl_a_944676_f0004_b.gif)