Abstract
Combining theoretical and experimental methods, the effects of 5 vol.-% WC dopant on the microstructure evolution, sintering behaviour and mechanical properties of ZrC ceramics were investigated. WC dopant was found to improve the high temperature elastic modulus and bending strength of ZrC ceramics. Both calculations and experimental results showed that the formation of (Zr, W)C solid solution promote dissolution of the impurity oxygen from the starting powder into the lattice sites, resulting in less oxygen defects in grain boundaries. Internal friction curve can also conform that the ZrC ceramics doped with WC have cleaner grain boundaries, which improved higher elastic modulus and bending strength in WC doped ZrC ceramics at elevated temperature.