Ignition and Combustion Characteristics of Nanoscale Al/AgIO3: A Potential Energetic Biocidal System

, , , , &
Pages 285-302 | Received 21 Jan 2010, Accepted 24 May 2010, Published online: 23 Dec 2010
 

Abstract

The authors investigated the ignition and reaction of Al/AgIO3 thermites for potential use in biocidal applications. Rapid-heating wire experiments were performed to measure the ignition temperature and investigate the thermal decomposition of the oxidizer using a T-Jump/TOF Mass Spectrometer and an optical emission setup. Combustion experiments inside a constant-volume pressure cell were also carried out, and the relative performance was compared with other thermite systems. The ignition temperature in air at atmospheric pressure was found to be 1215 ± 40 K. The AgIO3 was found to significantly outperform CuO and Fe2O3 oxidizers in pressurization tests, and this is attributed to the enhanced gas release as the AgIO3 thermally decomposes to release iodine in addition to oxygen. The reacted product was collected to investigate the final state of the products. Transmission electron microscopy and X-ray diffraction were performed to show that the major Ag product species was AgI, and not elemental Ag and I2. The AgI was found to be surface exposed to the environment, existing primarily as agglomerated spherical nanoparticles, and was found in some cases to coat the Al2O3 after the reaction.

ACKNOWLEDGMENTS

This work was funded by the Defense Threat Reduction Agency Basic Research Program. The authors also thank Kelvin Higa, Dan Kline, and Dan Bliss at the Naval Air Warfare Center for preparation of some of the thermite materials, and assistance with SEM/EDX and DSC-TGA analysis. They thank Dr. William Fourney for use of the high-speed camera. The authors acknowledge the support of the Maryland NanoCenter and its NispLab. The NispLab is supported in part by the NSF as a MRSEC Shared Experimental Facility.

Notes

a Al2O3 involves dissociation into several gaseous products (e.g., AlO, Al2O, O, O2), rather than molecular Al2O3.

b The product libraries do not contain some volatile species such as AlOI or AgI, and this may slightly affect the value.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 1,493.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.